Série Hastelloy

Hastelloy N

    Fil: 0.04-10mm

    Bande: 0.05-15mm*3-600mm 

    Barre: 3mm~800mm;

    Wire: 0.04-10mm

    Strip: 0.05-15mm*3-600mm 

    Bar: 3mm~800mm;

Hastelloy N alliage en acier:

Désignations équivalantes: UNS N10003
Fil: 0.04-10mm
bande: 0.05-15mm*3-600mm 
Barre: 3mm~800mm;
Pipe: OD 1 - 1000 mm; Epaisseur 0.1 - 100 mm
Feuille: Thickness 0.15-180mm; Largeur 8-3000mm; Longueur 500mm-11000mm
Traitement de surface: Noir, Brillant poli; Rugueur touné Rough Turned, No 4 Fini, Mat Fini, bA Fini, ou autres Finis

liste de produit et norme:

Equivalent designations: UNS N10003
Wire: 0.04-10mm
Strip: 0.05-15mm*3-600mm 
Bar: 3mm~800mm;
Pipe: OD 1 - 1000 mm; Thickness 0.1 - 100 mm
Sheet: Thickness 0.15-180mm; Width 8-3000mm; Length 500mm-11000mm

Surface Treatment: Black, Bright polished, Rough Turned, No 4 Finished, Matt Finished, bA Finished, or other Finished.

Hastelloy N Alloy Steel:

Product list and standard:

Elément chimique pour fusible automobile:

Propriétés physiques:

Méthode de traitement:

Matières premières → fonderie → dessin → laminage → recuit → produit fini → détection → emballage → expédition




Chemical element for automotive fuse:

Physical properties:


Processing method: 

Raw material→ Smelting→ Drawing→ Rolling→ Annealing→ Finished product→ Detection→ Packing→ Shipping


Les produits en métal de Shanghai sont emballés et étiquetés selon les règlements et les demandes du client. Un grand soin est pris pour éviter tout dommage qui pourrait être causé pendant le stockage ou le transport.

En outre, des étiquettes claires sont étiquetées à l'extérieur des emballages pour faciliter l'identification du produit I. D. et de l'information de qualité.

1) Shanghai Metal standard

2) personnalisation


Shanghai Metal Products are packed and labeled according to the regulations and customer's requests. Great care is taken to avoid any damage which might be caused during storage or transportation.

In addition, clear labels are tagged on the outside of the packages for easy identification of the product I. D. and quality information.

1)Shanghai Metal Standard





Contenants pour sels de fluorure fondu

Turbines à gaz

Industrie pétrochimique

Fours industriels

Équipement de traitement thermique

Génie nucléaire

Chambres de combustion des moteurs à réaction

Réchauffeurs de cabine d'aéronef

Composants d'échappement de turbine





Containers for molten fluoride salts

Gas turbines

Petrochemical industry

Industrial furnaces

Heat treating equipment

Nuclear engineering

Jet engine combustion chambers

Aircraft cabin heaters

Turbine exhaust components


Advantages and Features: 

HASTELLOY N alloy (UNS N10003) is a nickel-base alloy that was invented at Oak Ridge National Laboratories as a container material for molten fluoride salts. It has good oxidation resistance to hot fluoride salts in the temperature range of 1300 to 1600°F (704 to 871°C).

In tests of over two years duration, corrosion attack on HASTELLOY N alloy in molten fluoride salts at temperatures up to 1300°F (704°C), was less than one mil per year. It is expected that alloy N will be most useful in environments involving fluorides at high temperatures; however, the alloy compares favorably with other HASTELLOY alloys in various corrosive media, as shown in the table of penetration rates. Corrosion test samples of the alloy are available from any of the locations listed on the back cover of this technical information. It is especially suggested that the alloy be tested in molten halides of zirconium, beryllium, lithium, sodium, potassium, thorium or uranium.

HASTELLOY N alloy has good oxidation resistance in air. It shows promise for continuous operations at temperatures up to 1800°F (982°C). Intermittent use at temperatures up to 1900°F (1038°C) may also be possible. No discernible oxidation could be measured for the alloy at temperatures up to 1200°F (649°C).

Metallographic examinations have shown that the elements in alloy N remain in solid solution in the 1100 to 1600°F (593 to 871°C) range. Tensile tests have indicated no tendency toward embrittlement for prolonged periods at 1500°F (816°C). Alloy N has good weldability and can be readily forged. The hot working range is between 1600 and 2150°F (871 to 1177°C). It has been successfully extruded and further processed into high-quality seamless or manufactured as welded and drawn tubing.

Solution heat-treatment is recommended after hot or cold working of HASTELLOY N alloy parts. For sheet and plate, this is accomplished by soaking at 2150°F (1177°C) [sections up to 1/4 inch thick] and then cooling rapidly in air, or at 2165°F (1185°C) [sections 1/4 inch and thicker] followed by waterquenching.

HASTELLOY N alloy can be supplied, to order, in the forms of sheet, plate, and bar


HASTELLOY N alloy sheet, plate, bar, rod, and welded and seamless wrought pipe and tubing have been approved for use in the construction of unfired pressure vessels in accordance with the requirements of the ASME Boiler and Pressure Vessel Code Section VIII under Case 1315 (Special Ruling). Alloy N is approved for use at temperatures up to 1300°F (704°C).